Colorants for use in tinted contact lenses and methods for their production

ABSTRACT

The invention provides a colorant for use in tinting contact lenses in which the binding polymer used is capable of forming an interpenetrating polymer network with the lens material. When the colorants of the invention are applied to uncured lens material that is subsequently cured, the binding polymer forms an interpenetrating polymer network with the lens material embedding the colorant within the lens material resulting in a stable, tinted lens.

FIELD OF THE INVENTION

[0001] The invention relates to colorants useful in the production of tinted contact lenses. In particular, the invention provides a one step process for tinting contact lenses and colorants for use in the process.

BACKGROUND OF THE INVENTION

[0002] The use of tinted contact lenses to alter the natural color of the iris is well known. Generally, the tinted portion of the lens is located in the center of the lens, which portion of the lens will overlay either or both the pupil and iris of the lens wearer.

[0003] Colorants used to produce tinted lenses generally are composed of a binding polymer and pigments. The known colorants require the use of crosslinking agents to form covalent bonds between the lens materials and the binding polymer in order to form stable, tinted lenses. By “stable, tinted lenses” is meant that the tints do not bleed or leach out from the lens or from one portion of the lens to another. Additionally, in some of the known methods for forming tinted lenses, it is required that the lens body be formed prior to the introduction of the colorant onto the lens. Other processes and colorants require multiple steps for use alone or in conjunction with specialized rings to protect the outer portions of the lens from the colorant.

[0004] Thus, the known colorants and processes for producing tinted lenses introduce one or both of additional time and additional materials into the normal lens manufacturing process. Therefore, a need exists for a colorant, and method for producing contact lenses using the colorant, that eliminate some or all of these disadvantages.

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS

[0005] The invention provides colorants for use in the manufacture of tinted contact lenses, and a method for the tinting of contact lenses using the colorants of the invention. When the colorants of the invention are applied to uncured lens material that is subsequently cured, the binding polymer forms an interpenetrating polymer network with the lens material. Thus the colorant becomes embedded within the lens material resulting in a stable, tinted lens. This is advantageous in that the colorants do not require the use of covalent bonds to aid in the entrapment of the colorant's pigment within the lens. Further, the colorants of the invention transfer from a mold surface to the lens material in a way that results in a finished lens with a high resolution image of the pattern printed using the colorant.

[0006] In one embodiment, the invention provides a colorant for use in tinting contact lenses, the colorant comprising, consisting essentially of, and consisting of one or more pigments, one or more solvents, and a binding polymer, wherein the binding polymer is capable of forming an interpenetrating polymer network with a lens material. In another embodiment, the invention provides a method for manufacturing a tinted contact lens comprising, consisting essentially of, and consisting of the steps of; a.) applying to a molding surface of a mold a tinting-effective amount of a colorant, the colorant comprising, consisting essentially of, and consisting of: one or more pigments, one or more solvents and a binding polymer; b.) dispensing a lens-forming amount of a lens material into the mold; c.) swelling the colorant in the lens material; and d.) curing the lens material in the mold under conditions suitable to form the tinted contact lens, wherein the binding polymer and the lens material form an interpenetrating polymer network. In yet another embodiment, the invention provides a mold for use in manufacturing a tinted contact lens comprising, consisting essentially of, and consisting of a first and second mold half, wherein at least one molding surface of the first and second mold halves comprises, consists essentially of, and consists of one or more pigments, one or more solvents, and a binding polymer, wherein the binding polymer is capable of forming an interpenetrating polymer network with a lens material.

[0007] For purposes of the invention, by “interpenetrating polymer network” or “IPN” is meant an intimate network of two or more polymers at least one which is synthesized, crosslinked, or both in the presence of the other. For purposes of the invention, by “molding surface” is meant a mold surface used to form a surface of a lens.

[0008] It is a discovery of the invention that by using a binding polymer that is capable of forming an interpenetrating polymer network with a lens material, the need for formation of covalent bonds between the colorant and lens material to form a stable, tinted lens is eliminated. The binding polymers of the invention are made from a homopolymer, a mixture of monomers, copolymers, or combinations thereof containing functional groups that render the polymers and copolymers of the binding polymer capable of interactions with each other that are polar, dispersive, or of a charge transfer complex nature. The functional groups may be located on the polymer or copolymer backbones or be pendant from the backbones. The functional groups must be such that the groups of one polymer or copolymer interact with that of another in a manner that increases the density of the interactions helping to entrap the pigment particles.

[0009] For example, a monomer, or mixture of monomers, that form a polymer with a positive charge may be used in conjunction with a monomer or monomers that form a polymer with a negative charge to form the binding polymer. As a more specific example, methacrylic acid (“MAA”) and 2-hydroxyethylmethacrylate (“HEMA”) may be used to provide a MAA/HEMA copolymer that is then mixed with a HEMA/3-(N,N-dimethyl)propyl acrylamide copolymer to form the binding polymer.

[0010] As another example, the binding polymer may be composed of hydrophobically-modified monomers including, without limitation, amides and esters of the formula:

CH₃(CH₂ )_(x)—L—COCHR═CH₂

[0011] wherein L may be —NH or oxygen, x may be a whole number from 2 to 24, R may be a C₁ to C₆ alkyl or hydrogen and preferably is methyl or hydrogen. Examples of such amides and esters include, without limitation, lauryl methacrylamide, and hexyl methacrylate. As yet another example, polymers of aliphatic chain extended carbamates and ureas may be used to form the binding polymer.

[0012] Preferred binding polymers of the invention are a random block copolymer of HEMA, MAA and lauryl methacrylate (“LMA”), a random block copolymer of HEMA and MAA or HEMA and LMA, or a homopolymer of HEMA. The weight percentages, based on the total weight of the binding polymer, of each component in these embodiments is about 93 to about 100 weight percent HEMA, about 0 to about 2 weight percent MAA, and about 0 to about 5 weight percent LMA.

[0013] The molecular weight of the binding polymer must be such that its solubility in the lens material used is very low. However, at the same time, the molecular weight cannot be so high as to impact the quality of the printed image. Preferably, the molecular weight of the binding polymer is about 5,000 to about 1,000,000, more preferably about 7,000 to about 40,000, most preferably about 17,000 to about 30,000.

[0014] For purposes of the invention, the molecular weight is determined using a gel permeation chromatographer with a 90° light scattering and refractive index detectors. Two columns of PW4000 and PW2500, a methanol-water eluent of 75/25 wt/wt adjusted to 50mM sodium chloride and a mixture of polyethylene glycol and polyethylene oxide molecules with well defined molecular weights ranging from 325,000 to 194 are used. Alternatively, the molecular weights may be determined using a gel permeation chromatographer with a refractive index detector, a series of phenogel columns of 100 Å, 500 Å, 1,000 Å, and 10,000 Å, a tetrahydrofuran eluent and a polymethylmethacrylate standard ranging from 1.6E06 to 1,400 molecular weight.

[0015] One ordinarily skilled in the art will recognize that, by using chain transfer agents in the production of the binding polymer, by using large amounts of initiator, by using living polymerization, by selection of appropriate monomer and initiator concentrations, by selection of amounts and types of solvent, or combinations thereof, the desired binding polymer molecular weight may be obtained. Preferably, a chain transfer agent is used in conjunction with an initiator, or more preferably with an initiator and one or more solvents to achieve the desired molecular weight. Alternatively, small amounts of very high molecular weight binding polymer may be used in conjunction with large amounts of solvent to maintain a desired viscosity for the binding polymer. Preferably, the viscosity of the binding polymer will be about 4,000 to about 15,000 cps at 23° C.

[0016] Chain transfer agents useful in forming the binding polymers used in the invention have chain transfer constants values of greater than about 0.01, preferably greater than about 7, and more preferably greater than about 25,000. Suitable such chain transfer agents are known and include, without limitation, aliphatic thiols of the formula R—SH wherein R is a C₁ to C₁₂ aliphatic, a benzyl, a cyclicalipahtic or CH₃(CH₂)_(x) —SH wherein x is 1 to 24, benzene, n-butyl chloride, t-butyl chloride, n-butyl bromide, 2-mercapto ethanol, 1-dodecyl mercaptan, 2-chlorobutane, acetone, acetic acid, chloroform, butyl amine, triethylamine, di-n-butyl sulfide and disulfide, carbon tetrachloride and bromide, and the like, and combinations thereof. Generally, about 0.1 to about 7 weight percent based on the total weight of polymer formulation will be used.

[0017] Any desirable initiators may be used including, without limitation, ultra-violet, visible light, thermal initiators and the like and combinations thereof Preferably, a thermal initiator is used, more preferably 2,2-azobis isobutyronitrile and 2,2-azobis 2-methylbutyronitrile. The amount of initiator used will be about 0.1 to about 5 weight percent based on the total weight of the formulation. Preferably, 2,2-azobis 2-methylbutyronitrile is used with dodecanethiol.

[0018] The binding polymers of the invention may be made by any convenient polymerization process including, without limitation, radical chain polymerization, step polymerization, emulsion polymerization, ionic chain polymerization, ring opening, group transfer polymerization, atom transfer polymerization, and the like. Preferably, a thermal-initiated, free- radical polymerization is used. Conditions for carrying out the polymerization are within the knowledge of one ordinarily skilled in the art.

[0019] Solvents useful in the production of the binding polymer are medium boiling solvents having boiling points between about 120 and 230° C. Selection of the solvent to be used will be based on the type of binding polymer to be produced and its molecular weight. Suitable solvents include, without limitation, acetone, diacetone alcohol, cyclohexanone, tetrahydrofuran, ethyl acetate, isopropyl lactate, 3-methoxy 1-butanol, isopropanol, 1-ethoxy-2-propanol, and the like.

[0020] The binding polymer of the invention is tailored, in terms of expansion factor in water, to the lens material with which it will be used. Matching or substantially matching the expansion factor of the binding polymer with that of the lens material in the cured lens in packing solution avoids the development of stresses within the lens that result in bad optics and lens parameter shifts. Additionally, the binding polymer must be swellable in the lens material, permitting swelling of the image printed using the colorant of the invention. Due to this swelling, the image becomes entrapped within the lens material without any impact on lens comfort.

[0021] Pigments useful with the binding polymer in the colorants of the invention are those organic or inorganic pigments suitable for use in contact lenses, or combinations of such pigments. The opacity may be controlled by varying the concentration of the pigment and opacifying agent used, with higher amounts yielding greater opacity. Illustrative organic pigments include, without limitation, pthalocyanine blue, pthalocyanine green, carbazole violet, vat orange #1, and the like and combinations thereof. Examples of useful inorganic pigments include, without limitation, iron oxide black, iron oxide brown, iron oxide yellow, iron oxide red, titanium dioxide, and the like, and combinations thereof In addition to these pigments, soluble and non-soluble dyes may be used including, without limitation, dichlorotriazine and vinyl sulfone-based dyes. Useful dyes and pigments are commercially available.

[0022] Coating, or wetting, of the pigment particles with the binding polymer may be achieved by use of electrostatic, dispersive, and hydrogen bonding to cover the pigment's surface. Preferably, a high shear force is used to disperse the pigment into the binding polymer. The pigment may be added to the binding polymer by dispensing the polymer and pigment into a suitable mixer, such as a rotary shaft mixer and mixing until a homogeneous mixture results, typically for a period of up to about 30 minutes. The mixture may be then fed into a high shear mill, such as an Eiger mill to disperse the pigment into the binding polymer. Repeated milling is carried out as necessary to achieve complete dispersion. Generally, milling is carried out until the pigments are about 0.2 to about 3 microns in size. Milling may be carried out using any suitable, commercially available device including, without limitation, a high shear or ball milling device.

[0023] In addition to the pigment and binding polymer, the colorant of the invention contains one or more solvents that aid in coating of the colorant onto a surface. It is another discovery of the invention that, to ensure a colorant that does not bleed or run on the surface to which it is applied, it is desirable, and preferred, that the colorant have a surface tension below about 27 mN/m. This surface tension may be achieved by surface treatment of the surface, for example a mold surface, to which the colorant will be applied to increase the surface's wettability. Alternatively, and preferably, the desired surface tension may be achieved by the choice of solvents used in the colorant.

[0024] Thus, the solvents useful in the colorant of the invention are those solvents that are capable of increasing or decreasing the viscosity of the colorant and aiding in controlling the surface tension. Suitable solvents include, without limitation, cyclopentanones, 4-methyl-2-pentanone, 1-methoxy-2-propanol, 1-ethoxy-2-propanol, isopropyl lactate and the like and combinations thereof. Preferably, 1-ethoxy-2-propanol and isopropyl lactate are used.

[0025] In a preferred embodiment, at least three different solvents are used in the colorant of the invention. The first two of these solvents, both medium boiling point solvents, are used in the production of the binding polymer. Although these solvents may be stripped from the binding polymer after its formation, it is preferred that they are retained. Preferably, the two solvents are 1-ethoxy-2-propanol and isopropyl lactate. An additional low boiling solvent, meaning a solvent the boiling point of which is between about 75 and about 120° C., is used to decrease the viscosity of the colorant as desired. Suitable low boiling solvents include, without limitation, 2-propanol, 1-methoxy-2-propanol, 1-propanol, and the like and combinations thereof Preferably, 1-propanol is used.

[0026] The specific amount of solvents used will depend on a number of factors. For example, the amount of solvents used in forming the binding polymer will depend upon the molecular weight of the binding polymer desired and the constituents, such as the monomers and copolymers, used in the binding polymer. The amount of low boiling solvent used will depend upon the surface tension desired for the colorant. Further, if the colorant is to be applied to a mold and cured with a lens material, the amount of solvent used will depend upon the lens and mold materials used and whether the mold material has undergone any surface treatment to increase its wettability. Determination of the precise amount of solvent to be used is within the skill of one ordinarily skilled in the art. Generally, the total weight of the solvents used will be about 40 to about 75 weight percent of solvent will be used.

[0027] One ordinarily skilled in the art will recognize that each pigment used will have a critical pigment volume for the solvents selected. The critical pigment volume may be determined by any known means and, generally, is a volume based on the efficiency of a solvent and the binding polymer to suspend the pigment particles for example, as disclosed in Patton, Temple C., Paint Flow and Pigment Dispersion, 2d ed., pp 126-300 (1993).

[0028] In addition to the solvents, a plasticizer may be and, preferably is, added to the colorant to reduce cracking during the deoxygenation or drying of the colorant and optical mold parts, to enhance the final quality of the image produced using the colorant, and to enhance the diffusion and swelling of the colorant by the lens material. The type and amount of plasticizer used will depend on the molecular weight of the binding polymer used and, for colorants placed onto molds that are stored prior to use, the shelf-life stability desired. Useful plasticizers include, without limitation, glycerol, propylene glycol, dipropylene glycol, tripropylene glycol, polyethylene glycol 200, 400, or 600, and the like and combinations thereof Preferably, glycerol is used. Amounts of plasticizer used generally will be about 0.25 to about 10 weight percent based on the weight of the colorant.

[0029] The opacity of the colorant may be controlled by varying the pigment concentration and the pigment particle size used. Alternatively, an opacifying agent may be used. Suitable opacifying agents, such as for example titanium dioxide, are commercially available.

[0030] In a preferred colorant mixture of the invention, about 0.25 to about 25 weight percent of pigment, about 30 to about 45 weight percent of binding polymer, about 40 to about 70 weight percent of solvents, about 0 to about 25 weight percent of titanium dioxide, and about 0.25 to about 7 weight percent of plasticizer is used. The weight percentages are based on the total weight of the colorant mixture.

[0031] The binding polymer may be loaded with about 0.25 to about 25 weight percent based on the weight of the colorant for organic pigments and about 0.25 to about 50 weight percent for inorganic pigments. However, high pigment concentrations may impart a very dark hue. Therefore, preferably about 0.25 to about 7 weight percent of organic pigments and about 0 to about 20 weight percent of inorganic pigments are used. Combinations of pigments may be used in ratios dependent upon the color, shade, and hue desired.

[0032] One ordinarily skilled in the art will recognize that additives other than those discussed also may be included in the colorant composition of the invention. Suitable additives include, without limitation, additives that aid flow and leveling, additives for foam prevention, additives for rheology modification, and the like, and combinations thereof.

[0033] The colorant of the invention becomes embedded in the lens material upon curing of the material. Thus, the colorant may embed closer to one the front or back surface of the lens formed depending on the surface of the mold to which the lens the colorant is applied. Additionally, one or more layers of colorant may be applied in any order. In yet another embodiment, a pre-polymer layer may be used in conjunction with the colorant. For example, in the method of the invention a clear, pre-polymer layer may be applied to the molding surface of a mold half prior to application of the colorant. The pre-polymer may be the same or different from the binding polymer. If the pre-polymer is different from the binding polymer, it must be compatible with the binding polymer and lens material in terms of expansion factor and swellability and it must be capable of swelling into the lens material. Depending upon the pre-polymer selected, it may be used to transfer additional pigments, that are the same or different than those used in the colorant, into the lens material.

[0034] The invention may be used to provide tinted hard or soft contact lenses made of any known lens material, or material suitable for manufacturing such lenses. Preferably, the lenses of the invention are soft contact lenses having water contents of about 0 to about 90 percent and Dk values of about 10 to about 300. More preferably, the lenses are made of monomers containing hydroxy groups, carboxyl groups, or both or be made from silicone-containing polymers, such as siloxanes, hydrogels, silicone hydrogels, and combinations thereof. Material useful for forming the lenses of the invention may be made by reacting blends of macromers, monomers, and combinations thereof along with additives such as polymerization initiators. Suitable materials include, without limitation, silicone hydrogels made from silicone macromers and hydrophilic monomers. Examples of such silicone macromers include, without limitation, polydimethylsiloxane methacrylated with pendant hydrophilic groups as described in U.S. Pat. Nos. 4,259,467; 4,260,725 and 4,261,875; polydimethylsiloxane macromers with polymerizable function described in U.S. Pat. Nos. 4,136,250; 4,153,641, 4,189,546; 4,182,822; 4,343,927, 4,254,248; 4,355,147; 4,276,402; 4,327,203; 4,341,889; 4,486,577; 4,605,712; 4,543,398; 4,661,575; 4,703,097; 4,837,289; 4,954,586; 4,954,587; 5,346,946; 5,358,995; 5,387,632; 5,451,617; 5,486,579; 5,962,548; 5,981,615; 5,981,675; and 6,039,913; and combinations thereof. They may also be made using polysiloxane macromers incorporating hydrophilic monomers such as those described in U.S. Pat. Nos. 5,010,141; 5,057,578; 5,314,960; 5,371,147 and 5,336,797; or macromers comprising polydimethylsiloxane blocks and polyether blocks such as those described in U.S. Pat. Nos. 4,871,785 and 5,034,461. All of the cited patents are hereby incorporated in their entireties by reference.

[0035] Suitable materials also may be made from combinations of oxyperm and ionoperm components such as is described in U.S. Pat. Nos. 5,760,100; 5,776,999; 5,789,461; 5,807,944; 5,965,631 and 5,958,440. Hydrophilic monomers may be incorporated into such copolymers, including 2-hydroxyethyl methacrylate (“HEMA”), 2-hydroxyethyl acrylate, N,N-dimethylacrylamide (“DMA”), N-vinylpyrrolidone, 2-vinyl-4,4′-dimethyl-2-oxazolin-5-one, methacrylic acid, and 2-hydroxyethyl methacrylamide. Additional siloxane monomers may be incorporated such as tris(trimethylsiloxy)silylpropyl methacrylate, or the siloxane monomers described in U.S. Pat. Nos. 5,998,498; 3,808,178; 4,139,513; 5,070,215; 5,710,302; 5,714,557 and 5,908,906. They may also include various toughening agents, UV blockers, and wetting agents. They can be made using diluents such as primary alcohols, or the secondary or tertiary alcohols described in U.S. Pat. No. 6,020,445. All of the cited patents are hereby incorporated in their entireties by reference.

[0036] The materials for making the contact lenses are well known and commercially available. Preferably, the material used is etafilcon A and the binding polymer is formed from linear random block copolymers of MAA, HEMA and lauryl methacrylate (“LMA”). Etafilcon A, disclosed in U.S. Pat. Nos. 4,680,336 and 4,495,313 incorporated herein in their entireties by reference, generally is a formulation of 100 parts by weight (“pbw”) HEMA, about 1.5 to about 2.5 pbw MAA, approximately 0.3 to about 1.3 pbw ethylene glycol dimethacrylate, about 0.05 to about 1.5 pbw 1,1,1,-trimethylolpropane trimethacrylate, and about 0.017 to about 0.024 pbw of blue-HEMA. More preferably etafilcon A is used with a linear random block copolymer of MAA, HEMA and LMA in a ratio of 0.47 MAA to 100 HEMA to 4.14 LMA.

[0037] A tinting-effective amount of the colorant is used which is an amount sufficient to impart the desired level of tint to the lens to be produced. Generally, about 0.5 mg to about 4.0 mg of colorant is used.

[0038] The colorant used in the lenses of the invention are applied to the lens surface by any convenient method. In a preferred method of the invention, a thermoplastic optical mold, made from any suitable material including, without limitation, polypropylene or polystyrene resin is used. A tinting-effective amount of the colorant is applied to the desired portion of the molding surface of the mold. Application may be carried out by any convenient means. Preferably, application is carried out by pad printing.

[0039] A lens-forming amount of a lens material is dispensed into the mold. By “lens-forming amount” is meant an amount sufficient to produce a lens of the size and thickness desired. Typically, about 10 to about 40 mg of lens material is used.

[0040] The colorant is swelled in the lens material. Preferably, the swelling is carried out under conditions suitable to swell the colorant to about 1 to about 4 times its dried thickness. Typically, such swelling may be achieved in from about 1 to about 30 minutes at about 40 to about 68° C.

[0041] The mold containing the lens material and colorant then is exposed to conditions suitable to form the tinted lens. The precise conditions will depend upon the components of the colorant and lens material selected and are within the skill of one of ordinary skill in the art to determine, Once curing is completed, the lens is released from the mold and may be equilibrated in a buffered saline solution.

[0042] A preferred method of manufacturing a tinted lens is carried out using pad printing as follows. A metal plate, preferably made from steel and more preferably from stainless steel, is covered with a photo resist material that is capable of becoming water insoluble once cured. The pattern for the colorant is selected or designed and then reduced to the desired size using any of a number of techniques such as photographic techniques, placed over the metal plate, and the photo resist material is cured. Conditions for carrying out the pattern etching are within the knowledge of one ordinarily skilled in the art.

[0043] Following the pattern, the plate is subsequently washed with an aqueous solution and the resulting image is etched into the plate to a suitable depth, for example about 20 microns. The colorant is then deposited onto the pattern to fill the depressions with colorant. A silicon pad of a suitable geometry and varying hardness, generally about 1 to about 10, is pressed against the image on the plate to remove the colorant and the colorant is then dried slightly by evaporation of the solvent. The pad is then pressed against the molding surface of an optical mold and the colorant s allowed to dry. The mold is degassed for up to 12 hours to remove excess solvents and oxygen after which the mold is filled with lens forming amount of a lens material. A complementary mold half is then used to complete the mold assembly and, after the printed image is allowed to swell, the mold assembly is exposed to conditions suitable to cure the lens material used.

[0044] The invention will be clarified further by consideration of the following, non-limiting examples.

EXAMPLES Example 1

[0045] Synthesis of Binding Polymer

[0046] To a 5 L glass container was added 2.65 wt percent of dodecanethiol, 1.56 wt percent lauryl methacrylate, 0.18 wt percent MAA, 37.69 wt percent 2-HEMA, and 42.35 wt percent isopropyl lactate and 10.59 wt percent 1-ethoxy-2-propanol as solvents. The mixture was premixed for 10 min. using a magnetic stirrer and then transferred to a 5 L stainless steel reactor with a built-in heating mantel and equipped with a mechanical stirrer, nitrogen inlet, reflux condenser, and a temperature sensor. The mixture was heated to a temperature of approximately 63° C. for approximately 25 min, at which point 3.0 wt percent of 2,2-azobis-2-methyl butyronitrile were added with residual isopropyl lactate. Nitrogen was introduced into the reactor to create a nitrogen blanket to be used during the remainder of the polymerization.

[0047] After approximately 17 to 19 hrs, 1.96 wt percent of glycerol were added to the reaction mixture and the mixture was stirred for approximately 30 min. Subsequently, the stirring and nitrogen supply were discontinued and the reaction mixture cooled to room temperature.

Example 2

[0048] Binding polymers similar to or the same as those of Example 1 were used to make the colorant formulations listed on the table below. Color- Color- Color- Color- Color- Color- ant 1 rant 2 rant 3 rant 4 rant 5 rant 6 Pthalo- 2 0 0 2 0 0 cyanine Blue Iron Oxide 0 10 0 3 5 0 Black Iron Oxide 0 0 3 15 5 0 Yellow Iron Oxide 0 0 8 0 5 0 Brown Iron Oxide 0 0 2 0 0 0 Red TiO₂ 0 5 5 5 5 0 Total 0 15 18 25 20 0 Pigments Binding 41.49 35.63 34.28 31.12 33.37 42.39 Polymer Isopropyl- 38.96 33.46 32.19 29.22 31.34 39.81 lactate 1-ethoxy-2- 9.74 8.37 8.05 7.31 7.84 9.95 propanol 1-propanol 6 6 6 6 6 6 Glycerol 1.96 1.96 1.96 1.96 1.96 1.96 

What is claimed is:
 1. A colorant for use in tinting contact lenses, the colorant comprising one or more pigments, one or more solvents, and a binding polymer, wherein the binding polymer is capable of forming an interpenetrating polymer network with a lens material.
 2. The colorant of claim 1, wherein the binding polymer comprises a molecular weight of about 7,000 to about 40,000.
 3. The colorant of claim 1, wherein the binding polymer comprises: CH₃(CH₂)_(x)—L—COCHR═CH₂ wherein L is —NH or oxygen, x is a whole number from 2 to 24, R is a C₁ to C₆ alkyl or hydrogen.
 4. The colorant of claim 1, wherein the binding polymer comprises a copolymer of methacrylic acid, 2-hydroxyethyl methacrylate, and lauryl methacrylate.
 5. The colorant of claim 1, wherein the binding polymer comprises a homopolymer of 2-hydroxyethyl methacrylate.
 6. The colorant of claim 1, 2, 4 or 5, wherein the one or more solvents comprises two medium boiling point solvents and one low boiling point solvent.
 7. The colorant of claim 4, wherein the medium boiling point solvents comprise 1-ethoxy-2-propanol and isopropyl lactate.
 8. The colorant of claim 1, 2, 4 or 5, further comprising a plasticizer and an opacifying agent.
 9. The colorant of claim 8, comprising about 0.25 to about 25 weight percent of the one or more pigments, about 30 to about 45 weight percent of the binding polymer, about 40 to about 70 weight percent of the one or more solvents, about 0 to about 25 weight percent of the opacifying agent, and about 0.25 to about 7 weight percent of the plasticizer.
 10. A colorant for use in tinting contact lenses, the colorant comprising one or more pigments, one or more solvents, and a binding polymer having a molecular weight of about 7,000 to about 40,000, wherein the binding polymer is capable of forming an interpenetrating polymer network with a lens material comprising etafilcon A.
 11. The colorant of claim 10, wherein the binding polymer comprises a copolymer of methacrylic acid, 2-hydroxyethyl methacrylate, and lauryl methacrylate.
 12. The colorant of claim 10, wherein the binding polymer comprises a homopolymer of 2-hydroxyethyl methacrylate.
 13. The colorant of claim 10, 11 or 12, wherein the one or more solvents comprises two medium boiling point solvents and one low boiling point solvent.
 14. The colorant of claim 13, wherein the two medium boiling point solvents comprise 1-ethoxy-2-propanol and isopropyl lactate.
 15. The colorant of claim 10, 11 or 12, further comprising a plasticizer and an opacifying agent.
 16. The colorant of claim 15, comprising about 0.25 to about 25 weight percent of the one or more pigments, about 30 to about 45 weight percent of the binding polymer, about 40 to about 70 weight percent of the one or more solvents, about 0 to about 25 weight percent of the opacifying agent, and about 0.25 to about 7 weight percent of the plasticizer.
 17. A method for manufacturing a tinted contact lens comprising the steps of: a.) applying to a molding surface of a mold a tinting-effective amount of a colorant comprising one or more pigments, one or more solvents and a binding polymer; b.) dispensing a lens-forming amount of a lens material into the mold; c.) swelling the colorant in the lens material; and c.) curing the lens material in the mold to form the tinted contact lens, wherein the binding polymer and the lens material form an interpenetrating polymer network.
 18. The method of claim 17, wherein the binding polymer has a molecular weight of about 7,000 to about 40,000 and the lens material comprises etafilcon A. 19 The method of claim 18, wherein the binding polymer comprises a copolymer of methacrylic acid, 2-hydroxyethyl methacrylate, and lauryl methacrylate.
 20. The method of claim 18, wherein the binding polymer comprises a homopolymer of 2-hydroxyethyl methacrylate.
 21. The method of claim 17 or 18, wherein the one or more solvents comprises two medium boiling point solvents and one low boiling point solvent.
 22. The method of claim 21, wherein the two medium boiling point solvents comprise 1-ethoxy-2-propanol and isopropyl lactate.
 23. A mold for use in manufacturing a tinted contact lens comprising a first and second mold half, wherein at least one molding surface of the first and second mold halves comprises one or more pigments, one or more solvents, and a binding polymer, wherein the binding polymer is capable of forming an interpenetrating polymer network with a lens material.
 24. The mold of claim 23, wherein the binding polymer has a molecular weight of about 7,000 to about 40,000.
 25. The mold of claim 23, wherein the binding polymer comprises a copolymer of methacrylic acid, 2-hydroxyethyl methacrylate, and lauryl methacrylate.
 26. The mold of claim 23, wherein the binding polymer comprises a homopolymer of 2-hydroxyethyl methacrylate.
 27. The mold of claim 25 or 26, wherein the one or more solvents comprises two medium boiling point solvents and one low boiling point solvent.
 28. The mold of claim 27, wherein the two medium boiling point solvents comprise 1-ethoxy-2-propanol and isopropyl lactate. 